LSAW Steel tiyo
Longitudinal Submerged-Arc soude tiyo asye
Itilizasyon: Itilize pou livrezon likid presyon ba, tankou dlo, gaz, ak lwil oliv.
Pwosesis:
LSAW – UO(UOE),RB(RBE),JCO(JCOE)
DSAW -Double Submerged arc soude
Estanda:API 5L, API 5CT, ASTM 53, EN10217, DIN 2458. IS 3589, GB/T3091, GB/T9711
Sètifika:EN10217 EN10217 2c EN10219
Dyamèt deyò:355.6mm% e2�� 1626mm
Epesè mi:8 -50mm
Longè:jiska 12m
Klas asye:
API 5L: GR B, X42,X46, X56, X60% 2cX65% 2cX70
ASTM A53: GR A, GR B, GR C
EN: S275, S275JR, S355JRH, S355J2H
GB: Q195% 2c Q215% 2c Q235, Q345, L175, L210, L245, L320, L360- L555
Sifas:Fizyon kosyon epoksidik kouch, epoksidik goudwon chabon, 3PE, disparisyon kouch, kouch bitumen, kouch lwil nwa dapre kondisyon kliyan an.
Tès:Analiz konpozan chimik, Pwopriyete mekanik (Fòs rupture final, fòs sede, elongasyon), Pwopriyete teknik (Tès plat, tès koube, tès kònen, tès enpak), Enspeksyon gwosè eksteryè, tès idrostatik, tès radyografi.
Sètifika Tès Mill:EN 10204/3.1B
Epesè miray la
API 5L liy tiyo
KLAS STEEL
API 5L PSL1/PSL2 GR B, X42, X46, X52, X60, X65, X70
STEEL KONPOZISYON CHIMIK
|
KLAS STEEL |
% pa mas, Maksimòm |
||||
|
C |
sizo |
Mn |
P |
S |
|
|
GR B |
0.26 |
0.40 |
1.20 |
0.030 |
0.030 |
|
X42 |
0.26 |
0.40 |
1.30 |
0.030 |
0.030 |
|
X46 |
0.26 |
0.40 |
1.40 |
0.030 |
0.030 |
|
X52 |
0.26 |
0.40 |
1.40 |
0.030 |
0.030 |
|
X56 |
0.26 |
0.40 |
1.40 |
0.030 |
0.030 |
|
X60 |
0.26 |
0.40 |
1.40 |
0.030 |
0.030 |
|
X65 |
0.26 |
0.40 |
1.45 |
0.030 |
0.030 |
|
X70 |
0.26 |
0.40 |
1.65 |
0.030 |
0.030 |
PWOPRIYETE MEKANIK
|
KLAS STEEL |
Fòs sede, min. psi (MPa) |
Fòs rupture, min. psi (MPa) |
Elongasyon nan 2 pous, min. % |
|
GR B |
245 |
415 |
|
|
X42 |
290 |
415 |
|
|
X46 |
320 |
435 |
|
|
X52 |
360 |
460 |
|
|
X56 |
390 |
490 |
|
|
X60 |
415 |
520 |
|
|
X65 |
450 |
535 |
|
|
X70 |
485 |
570 |
TÈS OBLIJE
Analiz chimik, tès mekanik, enspeksyon vizyèl, tès tansyon, chèk dimansyon
Tès Bend, Tès Flattenting, Tès Enpak, Tès DWT, Tès NDT
Tès idrostatik, Tès dite...
ASTM A53 Steel Tiyo
ASTM A53 GR B Steel Tiyo
STEEL KONPOZISYON CHIMIK
Asye a dwe konfòme yo ak kondisyon sa yo kòm konpozisyon chimik:
|
KLAS STEEL |
Konpozisyon Max, % |
||||||||
|
C |
Mn |
P |
S |
Taks |
Ni |
Kr |
Mouvman |
V |
|
|
GR B |
0.30 |
1.20 |
0.05 |
0.05 |
0.40 |
0.40 |
0.40 |
0.15 |
0.08 |
PWOPRIYETE MEKANIK
|
KLAS STEEL |
Fòs rupture, min, Psi (MPA) |
Sede fòs, min, psi, (MPA) |
|
GR B |
60 000 (415) |
350 000 (240) |