Klas:GR.B, X42, X46, X52, X56, X60, X65, X70 X80
Gwosè:
Soti Dyamèt Range: 1/2 pous --- 24 pous
Ranje epesè miray: SCH10,SCH20,SCH40,SCH STD,SCH80
Longè: 1m---18m
Kouch:Kouch 3PE, kouch 3PP, kouch FBE, kouch epoksidik, penti espesyal
Anviwònman aplikab:Patikilyèman apwopriye pou transpò lwil oliv ak gaz long-, ki gen ladan tiyo soumaren ak gwo-altitid rejyon frèt. Ekselan tanperati ki ba -diverite li asire pèfòmans ki estab anba tanperati ekstrèm.
Pwosesis fabrikasyon:Pwodui pa metòd tankou woule cho, desen frèt oswa ekspansyon cho. Pandan pwosesis fabrikasyon tiyo asye, tretman chalè oblije asire pwopriyete mekanik yo ak rezistans korozyon.
Soudi ak enstalasyon:Lè soude tiyo asye X65, yo ta dwe adopte teknik ak materyèl soude ki apwopriye pou asire ke fòs soude a matche ak materyèl debaz la, sa ki fè li apwopriye pou enstalasyon rapid ak reparasyon sou sit-.
Sekirite ak Ekonomi:Akòz gwo fòs li yo ak rezistans korozyon, tiyo tiyo X65 diminye depans antretyen ak amelyore sekirite ak benefis ekonomik sistèm tiyo jeneral la.
Konpozisyon chimik ak pwopriyete mekanik:
|
Estanda |
Klas |
Konpozisyon chimik (%) |
Fòs rupture (min) |
Sede fòs (min) |
|||
|
C Mn PS |
Mpa |
Mpa |
|||||
|
API 5L PSL1 (SMLS) |
A |
0.22 |
0.90 |
0.030 |
0.030 |
335 |
210 |
|
B |
0.28 |
1.20 |
0.030 |
0.030 |
415 |
245 |
|
|
X42 |
0.28 |
1.30 |
0.030 |
0.030 |
415 |
290 |
|
|
X46 |
0.28 |
1.40 |
0.030 |
0.030 |
435 |
320 |
|
|
X52 |
0.28 |
1. 40 |
0.030 |
0.030 |
460 |
360 |
|
|
X56 |
0.28 |
1.40 |
0.030 |
0.030 |
490 |
390 |
|
|
X60 |
0.28 |
1.40 |
0.030 |
0.030 |
520 |
415 |
|
|
X65 |
0.28 |
1.40 |
0.030 |
0.030 |
535 |
450 |
|
|
X70 |
0.28 |
1.40 |
0.030 |
0.030 |
570 |
485 |
|
|
Estanda |
Klas |
Konpozisyon chimik (%) |
Fòs rupture |
Sede fòs |
|||
|
C Mn PS |
Mpa |
Mpa |
|||||
|
API 5L PSL2 (SMLS) |
B |
0.24 |
1.20 |
0.025 |
0.015 |
415-655 |
245-450 |
|
X42 |
0.24 |
1.30 |
0.025 |
0.015 |
415-655 |
290-495 |
|
|
X46 |
0.24 |
1.40 |
0.025 |
0.015 |
435-655 |
320-525 |
|
|
X52 |
0.24 |
1. 40 |
0.025 |
0.015 |
460-760 |
360-530 |
|
|
X56 |
0.24 |
1. 40 |
0.025 |
0.015 |
490-760 |
390-545 |
|
|
X60 |
0.24 |
1. 40 |
0.025 |
0.015 |
520-760 |
415-565 |
|
|
X65 |
0.24 |
1.40 |
0.025 |
0.015 |
535-760 |
450-600 |
|
|
X70 |
0.24 |
1.40 |
0.025 |
0.015 |
570-760 |
485-635 |
|
|
X80 |
0.24 |
1. 40 |
0.025 |
0.015 |
625-825 |
555-705 |
|
|
|
Klas |
Klas |
Analiz Chimik (%) |
Mekanik Prop |
||||
|
C |
Mn |
P |
S |
Fòs rupture (Mpa) |
Fòs Sede (Mpa) |
|||
|
API 5L (ERW) |
PSL1 |
B |
0.26 |
1.20 |
0.030 |
0.030 |
Pi gran pase oswa egal a 415 |
Pi gran pase oswa egal a 245 |
|
X42 |
0.26 |
1.30 |
0.030 |
0.030 |
Pi gran pase oswa egal a 415 |
Pi gran pase oswa egal a 290 |
||
|
X46 |
0.26 |
1.40 |
0.030 |
0.030 |
Pi gran pase oswa egal a 435 |
Pi gran pase oswa egal a 320 |
||
|
X52 |
0.26 |
1.40 |
0.030 |
0.030 |
Pi gran pase oswa egal a 460 |
Pi gran pase oswa egal a 360 |
||
|
X56 |
0.26 |
1.40 |
0.030 |
0.030 |
Pi gran pase oswa egal a 490 |
Pi gran pase oswa egal a 390 |
||
|
X60 |
0.26 |
1.40 |
0.030 |
0.030 |
Pi gran pase oswa egal a 520 |
Pi gran pase oswa egal a 415 |
||
|
X65 |
0.26 |
1.45 |
0.030 |
0.030 |
Pi gran pase oswa egal a 535 |
Pi gran pase oswa egal a 450 |
||
|
X70 |
0.26 |
1.65 |
0.030 |
0.030 |
Pi gran pase oswa egal a 570 |
Pi gran pase oswa egal a 485 |
||
|
PSL2 |
B |
0.22 |
1.20 |
0.025 |
0.015 |
415-655 |
245-450 |
|
|
X42 |
0.22 |
1.30 |
0.025 |
0.015 |
415-655 |
290-495 |
||
|
X46 |
0.22 |
1.40 |
0.025 |
0.015 |
435-655 |
320-525 |
||
|
X52 |
0.22 |
1.40 |
0.025 |
0.015 |
460-760 |
360-530 |
||
|
X56 |
0.22 |
1.40 |
0.025 |
0.015 |
490-760 |
390-545 |
||
|
X60 |
0.22 |
1.40 |
0.025 |
0.015 |
520-760 |
415-565 |
||
|
X65 |
0.22 |
1.45 |
0.025 |
0.015 |
535-760 |
450-600 |
||
|
X70 |
0.22 |
1.65 |
0.025 |
0.015 |
570-760 |
485-635 |
||
|
X80 |
0.22 |
1.85 |
0.025 |
0.015 |
625-825 |
555-705 |
||
Baj popilè: api 5l psl2 x65 liy tiyo, Lachin api 5l psl2 x65 liy tiyo manifaktirè, Swèd, faktori